A solvent-free, moisture insensitive, super low viscosity, high strength, 100% solids, two-component injection resin. It meets ASTM-C-881 Types I, II & V, Grade 1, Class B & C. It also meets USDA specifications for use in food processing areas.
An excellent epoxy adhesive for use in crack repair by pressure injection or gravity feed.
Compliances
ASTM-C-881: Types I, II & V, Grade 1, Class B & C
Meets USDA specifications for use in food-processing areas
Features
Ultra long gel time
Economical - mixing and dispensing in pressure pot such as Lily LPI
Link to product TEST DATA
|
Usage
Pressure-injection of cracks in structural concrete, masonry, wood, etc.
Gravity-feed of cracks in horizontal concrete and masonry
Appearance
Component A - clear
Component B - dark amber
Shelf Life: 2 year in original unopened container
Storage Conditions: Store at 40-95°F (5-35°C). Condition material to 65-85°F (18-29°C) before using
Gel Time (60 g. mass): 2 hrs. at 73°F (23°C)
Coverage
1 gal./3.8 L of mixed epoxy yields 231 cu. in./3,746 cu. cm of epoxy.
Packaging
150 ml x 300 ml cartridges
1 gal./3.8 liter units (2/3 gal. A, 1/3 gal. B)
3 gal./11.4 liter units (2 gal. A, 1 gal. B)
15 gal./56.8 liter units (two 5 gal pails A, one 5 gal. pail B)
165 gal./624.6 liter units (two 55 gal. drums A, one 55 gal. drum B)
|
Application
TO PRESSURE INJECT CRACKS: Be sure the crack is open where ports are placed and not impacted with debris. Flushing cracks is detrimental and should not usually be done. Use automatic injection equipment for 2:1 ratio epoxy that will absolutely stay on ratio while under pressure. Carefully set surface or countersink ports on face of crack. Be sure the crack is open where ports are placed and not impacted with debris. Set the ports with PRO-POXY 300, 300 FAST or 300 PASTE, being careful not to obstruct the crack with epoxy. If feasible, also seal the back side of crack with PRO-POXY 300, 300 FAST or 300 PASTE. The PRO-POXY 300, 300 FAST or 300 PASTE is a cap sealing compound when used in this application.
A successful and profitable injection job depends largely on carefully placing the cap seal and ports, allowing the injection to proceed smoothly with no leaks. Allow the cap seal to fully cure. Cure time will depend on temperature and which cap sealing compound was used. Inject SLOW SET INJECTION RESIN, always starting at the lowest port. If the back side of the crack has been sealed, stay on a port as long as it is accepting epoxy. Cap adjoining ports as epoxy extrudes out of them, staying on the original port until the pump stalls out or the crack is completely filled.
TO GRAVITY-FEED CRACKS: Seal underside of slab prior to filling if cracks reflect through. Pour neat SLOW SET INJECTION RESIN into v-notched crack. Continue placement until completely filled.
|
Limitations
Minimum substrate temperature is 40°F/5°C
Do not thin. Solvents will prevent proper cure.
Minimum age of concrete must be 5-7 days, depending on curing and drying conditions, for mortar.
Do not seal slabs on grade with product. SLOW SET INJECTION RESIN is a vapor barrier.
|
Cleanup
EQUIPMENT: Uncured material can be removed with Unitex CITRUS CLEANER or other approved solvent. Cured material can only be removed mechanically.
MATERIAL: Collect with absorbent material. Flush area with water. Dispose of in accordance with local, state and federal disposal regulations.
|
First Aid
EYE CONTACT: Flush immediately with water for at least 15 minutes. Contact physician immediately.
RESPIRATORY CONTACT: Remove person to fresh air.
SKIN CONTACT: Remove any contaminated clothing. Remove epoxy immediately with a dry cloth or paper towel. Solvents should not be used as they carry the irritant into the skin. Wash skin thoroughly with soap and water.
CURED EPOXY RESINS ARE INNOCUOUS.
|
Cautions
Component A - Irritant
Component B - Corrosive
Product is a strong sensitizer. Use of safety goggles and chemical resistant gloves are recommended.
Use of a NIOSH/MSHA organic vapor respirator is recommended if ventilation is inadequate.
Avoid breathing vapors.
Avoid skin contact.
|