K.C. WHITE ACRYLIC
CURE 25% |
|
|
|
White pigmented acrylic curing and sealing compound
|
|
Compliances
TT-C-800A Type II Class B
ASTM-C-309 Type II, Class B, White Pig
AASHTO-M-148 Type II, Class B, White
NOVDOCK 13 YF
|
|
|
Description
A 25% solids, white pigmented acrylic curing and sealing compound that meets KC,
Mo., specifications, as well as ASTM-C-1315 and ASTM-C-309.
|
|
Features
- Helps seal out salt and protects concrete
- 25% solids provides maximum retention of mix water, ensuring normal hydration of cement
- Quick drying – average 25 minutes
- Ideal for hot and windy conditions
|
|
|
|
|
Usage
- Cures, seals, hardens and dustproofs fresh concrete
- Protects concrete from oils, acids, salt, alkalis, fungus, grease, spalling,
sudden rainfalls and UV discoloration
- Retards moisture exchange, helps prevent efflorescence
Coverage
300 sq. ft./gal. (7.4 sq. m/L)
Drying Time at 80°F/27°C
Dry to touch: 15 min.
Dry hard: 25 min.
Packaging
5 gal./18.9 L pails
55 gal./208 L drums
Cleanup
Clean sprayer with Unitex CITRI-CLEAN.
|
|
Application
METHOD: Spray uniformly to form a continuous film for best results.
CURING AND SELING NEWLY PLACED CONCRETE: Application should be made immediately
after finishing as soon as bleed water has disappeared and slab can support the weight
of an applicator. Apply at 300 sq. ft. per gal./7.4 sq. m per L.
Limitations
- Will not provide bond to cementitious adhesives. Tests should be conducted to determine bondability with new products.
- To achieve proper results, do not dilute product or alter in any way.
Cautions
- Contains petroleum distillate, keep away from heat and open flame.
- Avoid prolonged breathing of vapor or repeated skin contact.
- Use in well-ventilated area.
- For industrial use only.
|
|
|
|
|
Physical Properties
| |
K.C.ACRYLIC
WHITE PIG 800 |
Requirements: Type II, Class B |
| MIN |
MAX |
| Total solids, percent by weight of compound |
25 |
25 |
– |
| Pigment, percent by wight of total solids |
7 |
7 |
– |
| Fineness of grind |
20 |
6 |
– |
| Viscosity, seconds (Ford Cup) |
16 |
– |
20 |
| Drying time: |
| Set to touch, minutes |
15 |
– |
20 |
| Dry hard, minutes |
25 |
– |
45 |
| Flash point (°F) |
100+ |
81 |
– |
| Reflectance |
67 |
65 |
– |
| Rubber base ppts, percent by weight of total solids |
44 |
40 |
– |
| Unit moisture loss, g/sq. cm @ 72 hours |
0.037 |
– |
0.039 |
| Coverage rate: |
| Freshly place substrate, sq. ft./gal. |
300 |
300 |
– |
| Aged substrate (28 days or over), sq. ft./gal. |
100+ |
100 |
– |
| Alkali resistance, hours |
48+ |
48 |
– |
| Salt Spray (5% @ 95°F, hours) |
500+ |
500 |
– |
| Accelerated weathering, hours days equivalent |
21+ |
21 |
– |
|
|
|
|
|
|
|
|
|
|
|
|
|
|