PRO-POXY 50
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 1, Types I, II, IV, V
Class B, C		 Injection resin Z18 fluorescent tracer dye
Super low viscosity
High modulus		 30 min. 2:1
RECOMMENDED USE: Pressure injection of hairline cracks, delamination, gravity feed of cracks, epoxy resin binder for patching and overlay
PRO-POXY 100
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 1, Types I, II, IV, V
Class B, C		 Injection resin Low viscosity
High modulus		 30 min. 2:1
RECOMMENDED USE: Pressure injection of cracks in structural concrete and masonry, gravity feed of cracks, binder for mortar patching and overlay
SLOW SET INJECTION RESIN
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 1, Type I, II, V
Class B, C		 Injection resin Ultra long gel time, economical 2 hrs. 2:1
RECOMMENDED USE: Pressure injection of cracks in structural concrete and masonry, gravity feed of cracks, binder for mortar patching and overlay
PRO-POXY 204
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 2, Types I, II, IV, V
Class B, C		 Bonding agent, injection resin Medium viscosity, super strength, fast set 30 min. 1:1
RECOMMENDED USE: Structural bonding of fresh to hardened & old to old concrete
Structural crack repair for large cracks – .007-.030 in/.18-.76 mm
Vertical anchoring, structural adhesive
PRO-POXY 200
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 2, Types I, II
Class B, C		 Bonding agent, injection resin Super strength, moisture-insensitive, excellent adhesion, corrosion-inhibiting 30 min. 1:1
RECOMMENDED USE: Structural bonding of fresh to hardened & old to old concrete
Structural crack repair for larger cracks - .007-.030 in/.18-.76 mm
Vertical anchoring of rebar, dowels, threaded rod
Structural adhesive for concrete,masonry, metal, wood, etc.
SLOW SET BONDING AGENT
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 2, Types I, II, V
Class B, C		 Bonding agent Ultra long gel time, low exotherm, medium viscosity, high modulus, corrosion-inhibiting Up to 8 hrs. 2:1
RECOMMENDED USE: Structural bonding of fresh to hardened & old to old concrete
Corrosion inhibitor for steel
PRO-POXY TYPE III D.O.T.
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 1, Type III
Class B, C		 Low modulus bonding agent for concrete overlays Low viscosity, self-leveling
Low modulus for shock absorption
Excellent bond strength
Meets AASHTO-AGC-ARTBA		 15-30 min. in mass
1 hr. in thin film		 1:1
RECOMMENDED USE: Bonding skid-resistant overlays to bridges & elevated slabs
Epoxy mortar for patching, low-modulus bonding agent
BRIDGESEAL
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
  Epoxy healer/sealer Z18 fluorescent tracer dye
Stops chloride ion intrusion
Bridge cracks, safer mixing		 1 hr. 1:1
RECOMMENDED USE: Protects new concrete, extends service life of old in bridge decks, parking decks, floors, columns
PRO-POXY 300
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 3, Types I, II, IV, V
Class B, C		 Non-sag, thixotropic, non-abrasive, injectable anchoring gel For use in wet or damp holes
Free-thaw resistant, seismic
Close edge distance
For solid or hollow		 35 min. 1:1
RECOMMENDED USE: Chemical anchoring, cap seal & port setting epoxy
Pressure injection for cracks in structural concrete, bonding irregular surfaces
PRO-POXY 300 FAST
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 3, Types I, II*, IV, V*
Class A, B, C		 Non-sag, thixotropic, non-abrasive, injectable anchoring gel For use in wet or damp holes
Free-thaw resistant, seismic		 8 min. 1:1
RECOMMENDED USE: Chemical anchoring, cap seal & port setting epoxy
Pressure injection for cracks in structural concrete, bonding irregular surfaces
PRO-POXY 300 PASTE
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 3, Types I, II, IV, V
Class B, C		 Non-sag, non-abrasive structural paste adhesive Non-sag paste for vertical and overhead applications
Moisture-insensitive, thixotropic		 35 min. 1:1
RECOMMENDED USE: Cap seal and port setting epoxy, bonding irrecular surfaces
PRO-POXY 400
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 3, Types I, II*, IV, V*
Class A, B, C		 Cold weather epoxy acrylate hybrid anchoring gel Works below 0°F
Sets up in water-filled holes
Guns to -5°F
Styrene-free
4 hrs. at 0°F/-18°C
6 min. at 80°F/27°C		 10:1
RECOMMENDED USE: Heavy-duty anchoring of rebar, threaded rod and epoxy-coated smooth dowels in all brick, concrete or stone masonry; best choice for structural bonding of heavy loads
Grouting bolts, dowels and pins vertical and overhead, where rapid setting, fast turnaround are needed; performs in damp or water-filled holes
PRO-FLEX
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
Grade 2, Class B, C Semi-rigid control joint sealant Shaves easily, fast
Pourable, self-leveling
Excellent shock-absorption		 30 min. 1:1
RECOMMENDED USE: Filling and sealing saw-cut control joints, random cracks
Flexible, low-modulus adhesive
PRO-FLEX GEL
  APPLICATION FEATURES GEL TIME* MIX RATIO
  Semi-rigid sealant Non-sag gel, pick-proof
Easy to mix		 30 min. 1:1
RECOMMENDED USE: Security sealant
PRO-POXY 2000
 ASTM C-881 APPLICATION FEATURES GEL TIME* MIX RATIO
  Epoxy machine grout High strength, low exotherm
Deep pour capability
Good oil and chemical resistance		 3.5 hrs. Pre-packged
RECOMMENDED USE: Critical new-equipment installation
Quick turnaround regrouting of foundations subject to oils, chemicals
PRO-POXY 2500
  APPLICATION FEATURES GEL TIME* MIX RATIO
  Epoxy patching mortar Durable, low modulus
Withstands free/thaw cycles, semi-rigid, compatible with Type III overlays		 30 min. Pre-packged
RECOMMENDED USE: Patching concrete on bridge decks, parking decks, floors, columns and beams. Repairing spalled areas. Plant maintenance.

*Gel time is based on 2 oz. (60 g.) mass at 73°F ?° (23°C). Gel time is initial set time. Ultimate strength time and thin film set time will be longer.

All of these products meet USDA specifications for use in food processing areas.

UNITEX PRO-POXY products are named with numbers relating to their level of viscosity. Lower numbers, like PRO-POXY 50, are super low viscosity for hair line crack injection. PRO-POXY 204 approximates the consistency of pancake batter, and PRO-POXY 300 PASTE approximates the consistency of peanut butter. As the number in the name increases, the viscosity increases. (Exception: PRO-POXY 2000 has a flowable viscosity.) Viscosities are chosen to suit the job application. Epoxies of different viscosities than recommended may be used to suit unusual applications. Consult UNITEX Technical Services for more information.
 